Dyneon™ PFA (a polymer of tetrafluoroethylene and perfluorovinylether) has exceptional heat resistance, excellent electrical properties and excellent chemical and weather resistance. It is also used in several chemical industry and home appliance coatings applications. This product line was recently expanded to include ultra high purity (UHP) grades for applications requiring low metal and anion extractables and low outgassing.
|
|
   
| Product Name |
Flexural Modulus - MPa (psi) - Injection Molded Bars 23°C (0.5" x 0.125" x 5.0") - ASTM D 790 |
Melt Flow Index (MFI) |
Melting Point °C (°F) - ASTM 4591 |
Tensile Strength at Break - MPa (psi) - Microtensile specimen Rate = 2"/min. at 23°C - ASTM D 1708 |
| Dyneon™ PFA 6502 UHP
|
550 MPa (80,000 psi) |
2 g/10 min. |
310°C (590°F) |
30 MPa (4,350 psi) |
| Dyneon™ PFA 6502N
|
550 MPa (80,000 psi) |
2 g/10 min. |
310°C (590°F) |
30 MPa (4,350 psi) |
| Dyneon™ PFA 6502T
|
550 MPa (80,000 psi) |
2 g/10 min. |
310°C (590°F) |
30 MPa (4,350 psi) |
| Dyneon™ PFA 6502TA
|
- |
- |
- |
- |
| Dyneon™ PFA 6505N
|
- |
- |
- |
- |
| Dyneon™ PFA 6505T
|
550 MPa (80,000 psi) |
5 g/10 min. |
310°C (590°F) |
30 MPa (4,350 psi) |
| Dyneon™ PFA 6515 UHP
|
620 MPa (90,000 psi) |
15 g/10 min. |
310°C (590°F) |
26 MPa (3,770 psi) |
| Dyneon™ PFA 6515N
|
620 MPa (90,000 psi) |
15 g/10 min. |
310°C (590°F) |
26 MPa (3,770 psi) |
| Dyneon™ PFA 6515T
|
620 MPa (90,000 psi) |
15 g/10 min. |
310°C (590°F) |
26 MPa (3,770 psi) |
| Dyneon™ PFA 6525N
|
- |
25 g/10 min. |
310°C (590°F) |
21 MPa (3,050 psi) |
| Dyneon™ PFA 6900N
|
- |
- |
- |
- |
| Dyneon™ PFA-FLEX 8502 UHP
|
600 MPa (87,000 psi) |
2 g/10 min. |
290°C (554°F) |
35 MPa (5,075 psi) |
| Dyneon™ PFA-FLEX 8515 UHP
|
600 MPa (87,000 psi) |
15 g/10 min. |
290°C (554°F) |
34 MPa (4,930 psi) |
|
|
|