Skip to Primary Navigation Skip to Site Navigation Skip to Main Content
 
Products and Solutions
 

Fluoroelastomers Copolymers
Dyneon - Products - Fluoroelastomer Copolymers

Known for their excellent resistance to heat and aggressive chemicals, as well as outstanding processability and permeation resistance, Dyneon's full line of fluoroelastomers (FKMs) provides processors and end users flexibility in choosing the right material for critical sealing applications.

 

Product Features

  • Broad Chemical Resistance
  • Temperature resistance -18 to 250°C
  • Low permeation
   

 

Typical Applications

O-rings, seals, gaskets and hose for the following markets:

 

  • Automotive Powertrain
  • Transportation Fuel Systems
  • Lubricant Application
  • Chemical Processing
  • Oil and Gas Exploration
Typical PropertiesTechnical Data SheetsMSDSRelated Documents
Product Name Compression Set - % - 70 hrs @ 200°C - ASTM D395 Method B Cure Technology Mooney Viscosity - ML1 + 10 @ 121 °C Post Cure Press Cure Tensile MPa (psi)
Dyneon™ FC 2110Q 
19
Incorporated Cure
-
24 h @ 250°C
7 min @ 177°C
13.8 MPa (2,010 psi)
Dyneon™ FC 2120 
16
Incorporated Cure
23
24 h @ 250°C
7 min @ 177°C
14.7 MPa (2,140 psi)
Dyneon™ FC 2121 
14
Incorporated Cure
24
24 h @ 250°C
7 min @ 177°C
16.4 MPa (2,375 psi)
Dyneon™ FC 2122 
25
Incorporated Cure
25
24 h @ 250°C
7 min @ 177°C
13.1 MPa (1,900 psi)
Dyneon™ FC 2123 
20
Incorporated Cure
25
24 h @ 250°C
7 min @ 177°C
16.2 MPa (2,350 psi)
Dyneon™ FC 2144 
17
Incorporated Cure
41
24 h @ 250°C
7 min @ 177°C
17.5 MPa (2,540 psi)
Dyneon™ FC 2145 
16
Raw Gum
28
24 h @ 250°C
7 min @ 177°C
12.2 MPa (1,765 psi)
Dyneon™ FC 2152 
22
Incorporated Cure
51
24 h @ 250°C
7 min @ 177°C
14.5 MPa (2,100 psi)
Dyneon™ FC 2170 
18
Incorporated Cure
31
24 h @ 250°C
7 min @ 177°C
13.8 MPa (2,000 psi)
Dyneon™ FC 2174 
12
Incorporated Cure
40
24 h @ 250°C
7 min @ 177°C
16.9 MPa (2,450 psi)
Dyneon™ FC 2176 
22
Incorporated Cure
30
24 h @ 250°C
7 min @ 177°C
15 MPa (2,175 psi)
Dyneon™ FC 2177D 
21
Incorporated Cure
33
24 h @ 250°C
7 min @ 177°C
12.8 MPa (1,865 psi)
Dyneon™ FC 2178 
10
Raw Gum
100
24 h @ 250°C
7 min @ 177°C
15.7 MPa (2,275 psi)
Dyneon™ FC 2179 
10
Incorporated Cure
80
24 h @ 250°C
7 min @ 177°C
17.1 MPa (2,475 psi)
Dyneon™ FC 2180 
12
Incorporated Cure
40
24 h @ 250°C
7 min @ 177°C
16.3 MPa (2,370 psi)
Dyneon™ FC 2181 
13
Incorporated Cure
44
24 h @ 250°C
7 min @ 177°C
17.6 MPa (2,560 psi)
Dyneon™ FC 2182 
22
Incorporated Cure
30
24 h @ 250°C
7 min @ 177°C
13.5 MPa (1,960 psi)
Dyneon™ FC 2210X 
-
Raw Gum
-
24 h @ 250°C
7 min @ 177°C
-
Dyneon™ FC 2211 
17
Raw Gum
-
24 h @ 250°C
7 min @ 177°C
12.9 MPa (1,870 psi)
Dyneon™ FC 2230 
15
Raw Gum
38
24 h @ 250°C
7 min @ 177°C
13.7 MPa (1,995 psi)
Dyneon™ FC 2260 
25
Raw Gum
60
24 h @ 250°C
7 min @ 177°C
16.2 MPa (2,345 psi)
Dyneon™ FC 2261Q 
14
Raw Gum
63
24 h @ 250°C
7 min @ 177°C
12.9 MPa (1,870 psi)
Dyneon™ FE 5520X 
20
Incorporated Cure
26
24 h @ 260°C
5 min @ 170°C
13.8 MPa (2,000 psi)
Dyneon™ FE 5542X 
18
Raw Gum
42
24 h @ 260°C
5 min @ 170°C
14.5 MPa (2,100 psi)
Dyneon™ FE 5610 
21
Incorporated Cure
-
24 h @ 250°C
7 min @ 177°C
13.3 MPa (1,930 psi)
Dyneon™ FE 5620Q 
13
Incorporated Cure
23
24 h @ 250°C
7 min @ 177°C
15.4 MPa (2,240 psi)
Dyneon™ FE 5621 
13
Incorporated Cure
23
24 h @ 260°C
5 min @ 177°C
15.4 MPa (2,240 psi)
Dyneon™ FE 5622Q 
18
Incorporated Cure
22
24 h @ 250°C
7 min @ 177°C
16.2 MPa (2,350 psi)
Dyneon™ FE 5623 
13
Incorporated Cure
24
24 h @ 250°C
5 min @ 177°C
15.8 MPa (2,300 psi)
Dyneon™ FE 5640Q 
11
Incorporated Cure
40
24 h @ 250°C
7 min @ 177°C
16.3 MPa (2,370 psi)
Dyneon™ FE 5641Q 
11
Incorporated Cure
40
24 h @ 250°C
7 min @ 177°C
16.1 MPa (2,340 psi)
Dyneon™ FE 5642 
17
Incorporated Cure
42
24 h @ 250°C
7 min @ 177°C
17.4 MPa (2,530 psi)
Dyneon™ FE 5643Q 
11
Incorporated Cure
40
24 h @ 250°C
7 min @ 177°C
16.5 MPa (2,400 psi)
Dyneon™ FE 5660Q 
9
Incorporated Cure
60
24 h @ 250°C
7 min @ 177°C
16.5 MPa (2,400 psi)
Dyneon™ FG 5630Q 
13
Incorporated Cure
30
24 h @ 250°C
7 min @ 177°C
14.7 MPa (2,140 psi)
Dyneon™ FG 5661X 
14
Incorporated Cure
60
24 h @ 260°C
5 min @ 177°C
15.3 MPa (2,223 psi)
Dyneon™ FG 5690Q 
10
Incorporated Cure
97
24 h @ 250°C
7 min @ 177°C
16.3 MPa (2,360 psi)
Dyneon™ FX 3734 
23
Incorporated Cure
42
24 h @ 250°C
7 min @ 177°C
16 MPa (2,300 psi)
Dyneon™ FX 3735 
36
Incorporated Cure
42
24 h @ 250°C
7 min @ 177°C
15 MPa (2,150 psi)
Dyneon™ FX 11818 
34
Incorporated Cure
28
24 h @ 260°C
5 min @ 177°C
12.4 MPa (1,800 psi)
Product
Contact Dyneon

Need more
information?
Contact Us

Documents
Dyneon - Products - Fluoroelaastomers Dyneon™ Fluoroelastomers Product Selection Guide (PDF, 2.2MB)