3M™ Scotch-Weld™ Epoxy Adhesive DP405 is a toughened, two-part epoxy adhesive. 2:1 mix ratio, 5 minute work life and handling strength in 20 minutes. 3M™ Scotch-Weld™ EPX™ 400 mL applicator and mix nozzles are required for dispensing (not included).
  • 5 minute work life
  • High peel and shear strength
  • Toughened for impact resistance
  • General industrial, sporting goods, solar energy, wind energy, composites, electronics, military, transportation and aerospace
  • Bonding, gluing, joining, attaching, assembling, encapsulating, potting and sealing.
Need Help?

Questions? We can help

Contact Us

 
Is a fast setting adhesive that exhibits good shear and peel strengths along with good impact and durability. It bonds extremely well to many surfaces, such as metals, ceramics, wood and some plastics.

Specifications

ApplicationsHard Disk Drive Component Assembly
BrandScotch-Weld
ColorBlack
Consumer LabelNo
Container Volume400 ml
Full Cure24 Hours @ 72 F (22 C)
Hardness75 Shore D
IndustriesTransportation, Specialty Vehicle, Construction, Military & Government, General Industrial, Electronics, Consumer Goods
Mix Ratio Volume Base:Accelerator2 : 1
Peel Strength at 72 Degrees F (22 Degrees C)35 lb/in
Physical FormFlowable Liquid
Product FormCartridge
Shear Strength at 72 Degrees F (22 Degrees C)5300 Pound-Force Per Square Inch
Shelf Life in Months (from date of manufacture)15
Storage Temperature72 Degree Fahrenheit
Substrate 1Plastics (ABS, PVC, Acrylic), Metal, Glass & Ceramics
Substrate 2Plastics (ABS, PVC, Acrylic), Metal, Glass & Ceramics
Time to Handling Strength10 Minute
TypeEpoxy Adhesive
Viscosity Range (cps) at Room Temperature14,000
Worklife5 minutes @ 72 F (22 C)